0.5mm-50.8mm AISI 440C STAINLESS STEEL BALLS

Applications

Precision bearings, anti-friction bearings, special valves, conveyor belts and rollers, ballpoint pens. They are used in foodstuff, medical instruments, quick couplings, recirculating ball bearings, knotting devices, oil refinery devices. 

%C

%Si

%Mn

%P

%S

%Cr

%Mo

0.95-1.20 

1.00 max 

1.00 max 

0.040 max 

0.030 max 

16.00-18.00 

0.75 max 

ITA

USA

GER

FRA

UK

RUS

CHN

JAP

X 105CrMo17 

440C 

1.4125 

Z100CD17 

- 

95X18 

9Cr18Mo 

SUS440C 

Property

Symbol

U.o.M.

Type

Notes

Values

Density 

δ 

[g/cm3] 

Physical 

Room temp. 

7.75 

Young's modulus 

E 

[GPa] 

Mechanical 

- 

210 

Specific heat 

c 

[J/kg-K] 

Thermal 

Room temp. 

450 

Coefficient of linear thermal expansion 

α 

[10^-6/ºC] 

Thermal 

(ΔT=0-100°C) 

10.2 

Thermal conductivity 

λ 

[W/(m·K)] 

Thermal 

Room temp. 

19.6 

Electric resistivity 

ρ 

[Ω*m*10^-9] 

Electric 

- 

680 

Relative magnetic permeability 

µ 

- 

Magnetic 

Ferromagnetic 

> 700 

Property

Type

U.o.M.

Values

U.o.M.

Values

Hardness 

Mechanical 

[HRC] 

58 - 65 

- 

- 

Ultimate tensile strength 

Mechanical 

[MPa] 

1900 - 2000 

[psix10^3] 

275 - 290 

Service temperature 

Thermal 

[ºC] 

0 - 400 

[ºF] 

32 - 752 

Corrosion Resistance

The material resists to corrosion in contact with freshwater, steam, oil, petrol, alcool. They are subjected to pitting corrosion in sea water environments. Poor corrosion resistance in acid environments.